> Products > Printed Electronics
Performance | Remark | |
---|---|---|
Line width | 60 ~ 70 ㎛ | |
Resistivity | 0.7 ~ 2.5 X 10-4 Ω∙㎝ | Specific resistance |
Viscosity | 100,000 ~ 300,000 cps | Spinde 51, 0.4RPM |
Adhesion | 0 | Cross - cutting test(ISO2409) |
Hardness | above 3H | Pencil, 1Kg |
Product name | Silver Paste-HT 01 | Silver Paste-HT 02 |
---|---|---|
Adhesion mechanism | Containning PbO Glass Powder | Not ContainningPbO Glass Powder |
Solid contents(%) | 88±2 | 88±2 |
Viscosity(cps) Brookfield-Ⅱ+(spindle No.CPE51) @25℃,0.4rpm |
200,000~400,000 cps | 200,000~400,000 cps |
Curing temperature(℃) | 400~700℃ | 450~700℃ |
Resistivity(Ω∙㎝) | under 6 X 10-06 | under 6 X 10-06 |
Adhesion (ASTM)) | above 5B | above 5B |
Substrate | Glass, Ceramic substrate | |
Printing method | Screen printing(Line Resolution : above 70um) |
Products name | Silver nano Paste DGP-NO | Silver paste DGP-MS | ||
---|---|---|---|---|
Partivle size | nano | Submicron ~ Micron | ||
Solid contents(%) | 70±5 | 80±5 | ||
viscosity(cps) | 100,000±50,000 | 200,000±50,000 | ||
Substrate | PET Film | Glass | PET Film | Ceramic |
Curing condition(℃) | 120-150 | 200-300 | 120-150 | 300-400 |
Resistivity(uΩ•cm) | 10-50 | 2-10 | 10-50 | 5-30 |
Pattern Thickness(um) | 1 - 4 | 8 - 10 | ||
Printing method | Screen printing | Screen printing |
Properties | Specification | Remark |
---|---|---|
Solid contents | 75 ± 5 wt% | - |
Viscosity (0.4rpm) | 50,000~100,000cp | Brookfield HB spindle #51, Adjustable |
Shelf time | 3 months (refrigerated) | Stir in the paste before using |
Curing condition | 130℃ | IR : 10min / Oven : 20min |
Volume resistance | 10~50 (1~5 x 10-5Ω·cm) |
(uΩ·cm), 4 point probe |
Adhesion | 100/100 (PET, ITO film, ITO glass) | Cross cut or Taping |